Remaining life assessment issues in high Cr martensitic steels and development of new innovative tools for damage monitoring and integrity assessment
The relatively newer high Cr martensitic steels such as P91 have now been in use in power industry for over twenty years. Over this time, there have been a number of incidents of cracking and failure in components made from P91 steel, both in thick and thin section equipments mainly due to creep damage. The thick section components have been usually failing due to….